HBM 4265
Description
HBM 4265
High Density Polyethylene
Product Description
HBM 4265 is a high molecular weight, high-density polyethylene with broad molecular weight distribution specially developed for producing intermediate bulk containers (IBC) for the packaging of dangerous goods, large blow molding parts and jerry cans. This grade, which is produced by 1-hexene co-monomer, offers very good creep strength, chemical resistance and environmental stress cracking resistance (ESCR), good process-ability and stiffness. HBM 4265 has been produced under Basell license.
General Information
| Status | Commercial: Active | |
| Application
| Intermediate Bulk Container (IBC) – Large Agricultural Tank – Small to Large Jerry Cans
| |
| Form(s)
| Pellet | |
| Attribute | Very Good ESCR Very Good Creep Strength Good Chemical Resistance
| High Impact Resistance Easy Process-ability |
| Additives | Processing Aid: No Antioxidant: Yes | Antiblock: No Slip Agent: No |
| Typical Properties | Typical Value 1 | Unit | Test Method |
| High Load Melt Flow Index (190oC/ 21.6 kg) | 6.5 | g/10 min | ISO 1133 |
| Density 2 | 0.942 | g/cm3 | ISO 1183 |
| Bulk Density | > 0.50 | g/cm3 | ISO 60 |
| Mechanical 3 | |||
| Tensile Strength at Yield | 24 | MPa | ISO 527-1, -2 |
| Tensile Strength at Yield | 10 | % | ISO 527-1, -2 |
| Tensile Modulus of Elasticity | 800 | MPa | ISO 527-1, -2 |
| FNCT (3.5 MPa, 2% Arkopal N100, 80oC) | 60 | hr | ISO 16770 |
| Impact | |||
| Tensile Impact Strength (Notched, Type 1, Method A, -30oC) | 160 | kJ/m2 | ISO 8256 |
Thermal
| Melting Temperature | 130 | oC | ISO 3146 |
| Vicat Softening Temperature (Method A/ 10N) | 128 | oC | ISO 306 |
| Deflection Temperature Under Load (0.45 MPa) | 70 | oC | ISO 75 |
| Deflection Temperature Under Load (1.8 MPa) | 52 | oC | ISO 75 |
| Recommended Process Conditions 4 | |||
| Extruder Barrel Temperature: 200-230 °C | Melt Temperature: 205-235 °C | ||
- Typical values: these are not to be construed as
- The density parameter was determined on compression-molded specimens, which were prepared in accordance with procedure C of ASTM D4703, Annex A1.
- Properties are based on compression-molded specimens, which were prepared in accordance with procedure B of ASTM D4703, Annex A1, using 100% HBM 4265 resin.
- Please note that these processing conditions are recommended by manufacturer only for 100% HBM 4265 resin (not in the case of blending with any other compatible material), therefore because of the many particular factors which are outside our current knowledge and control and may affect the use of product, no warranty is given for the foregoing Also, the specific recommendations for resin type and the processing conditions can only be made when the end use, required properties and fabrication equipment are known.
Delivery Terms
Petroduct offers flexible international shipping options tailored to customer needs. Available delivery terms include:
FCA (Free Carrier)
CPT (Carriage Paid To)
FOB (Free On Board)
CFR (Cost and Freight)
All shipments are coordinated from designated ports with standard packaging and full compliance with customs and logistics requirements. For optimal delivery planning, please consult our sales team when placing your order.
Order Now
Downloads
TDS : Download
MSDS: Download