MFI 3713
MFI 3713 is a medium density polyethylene, which has a broad molecular weight distribution and high melt strength.
Description
MFI 3713
Medium Density Polyethylene
Product Description
MFI 3713 is a medium density polyethylene, which has a broad molecular weight distribution and high melt strength. This product which is produced by 1-hexene as a comonomer, specially designed for producing thin films with high tear resistance, good seal-ability, high strength and high draw down. This product is suitable for manufacturing of high strength carrier bags and high quality thin films for uni/multi-wall packaging. MFI 3713 has been manufactured under Basell license.
| General Information | ||
| Status | Commercial: Active | |
| Application | Blown film extrusion- Uni/multi wall packaging- High quality thin films- High strength carrier bags | |
| Form(s) | Pellet | |
| Attribute | High melt stability- Good tear resistance- High Strength and toughness. | |
|
Additives | Antioxidant: Yes Processing Aid: No | Antiblock: No Slip Agent: No |
| Typical Properties | Typical Value 1 | Unit | Test Method |
| Physical | |||
| High Load Melt Flow Index (190oC/ 21.6 kg) | 13 | g/10 min | ISO 1133 |
| Density 2 | 0.937 | g/cm3 | ISO 1183 |
| Mechanical 3 | |||
| Tensile Modulus of Elasticity | 735 | MPa | ISO 527-1,2 |
| Tensile Strength (MD) | 46 | MPa | ISO 527-1,3 |
| Tensile Strength (TD) | 46 | MPa | ISO 527-1,3 |
| Tensile Strain at Break (MD) | 550 | % | ISO 527-1,3 |
| Tensile Strain at Break (TD) | 650 | % | ISO 527-1,3 |
| Elmendorf Tear Strength (MD) | 210 | mN | ISO 6383-2 |
| Elmendorf Tear Strength (TD) | 1100 | mN | ISO 6383-2 |
| Failure Energy | 7 | J/mm | DIN 53373 |
| Dart Drop Impact | 120 | g | ASTM D1709 |
| Thermal | |||
| Melting Temperature | 127 | °C | ISO 3146 |
| Vicat Softening Temperature (Method A/10N) | 121 | °C | ISO 306 |
| Recommended Process Conditions 4 | |||
| Extruder temperature profile: 190-230 °C | Blow up ratio: 3-5 | ||
| Film thickness: 10-50 μm |
- Typical values: these are not to be construed as
- The density parameter was determined on compression-molded specimens, which were prepared in accordance with procedure C of ASTM D4703, Annex A1.
- Properties are based on 20 μm blown film produced at a melt temperature of 220°C and 3 BUR using 100% MFI 3713 resin. Modulus property is based on compression-molded specimens, which were prepared in accordance with procedure B of ASTM D4703, Annex
- Please note that, these processing conditions are recommended by manufacturer only for 100% MFI 3713 resin (not in the case of blending with any other compatible material), therefore because of the many particular factors which are outside our current knowledge and control and may affect the use of product, no warranty is given for the foregoing Moreover, the specific recommendations for resin type and processing conditions can only be made when the end use, required properties and fabrication equipment are known.
Additional information
| MFI (dg/min): |
13 (190 °C/ 21.6 Kg) |
|---|---|
| Density (kg/m3): |
937 |
| Application(s): |
Blown film extrusion, Uni/multi wall packaging, High quality thin films, High strength carrier bags |
Delivery Terms
Petroduct offers flexible international shipping options tailored to customer needs. Available delivery terms include:
FCA (Free Carrier)
CPT (Carriage Paid To)
FOB (Free On Board)
CFR (Cost and Freight)
All shipments are coordinated from designated ports with standard packaging and full compliance with customs and logistics requirements. For optimal delivery planning, please consult our sales team when placing your order.
Order Now
Downloads
TDS : Download
MSDS: Download